1. The quality of electroslag pressure welded joints does not meet the requirements

　?。ㄒ唬┈F象

　　(1) Phenomenon

　　接頭處軸線彎折或軸線偏疼過大，焊包不勻，并有咬邊、夾渣、未熔合等現象；鋼筋夾持處燒傷。

　　The bending or migration of the axes at the joints is too large, the welding package is uneven, and there are some phenomena such as undercut, slag inclusion, non-fusion, etc. The reinforcing bar is burned at the clamping position.

　　（二）原因剖析

　　(2) Cause analysis

　　1、鋼筋端部歪扭不直，整理不干凈或端面不平；鋼筋裝置不正，軸線偏移，機具損壞，造成鋼筋晃動和位移；焊接完成后，接頭未經充分冷卻；

　　1. The end of the reinforcing bar is not straight, clean or uneven; the installation of the reinforcing bar is not correct, the axis is offset, and the machine tool is damaged, resulting in the sway and displacement of the reinforcing bar; after welding, the joint has not been fully cooled;

　　2、焊接工藝方法使用不妥，焊接參數挑選不合適，操作技術不過關；

　　2. Improper use of welding technology, inappropriate selection of welding parameters and poor operation technology;

　　3、焊劑裝填不勻，或受潮。

　　3. Flux filling is uneven or damp.

　　（三）防治辦法

　　(3) Measures for prevention and control

　　1、焊接前應矯正或切除鋼筋端部過于彎折或歪曲的部分，并予以鏟除干凈，鋼筋端面應磨平；

　　1. Before welding, the bending or distorted part of the end of the reinforcing bar should be corrected or removed, and the end of the reinforcing bar should be eradicated, and the end face of the reinforcing bar should be ground flat.

　　2、鋼筋加工裝置應由持證焊工進行，裝置鋼筋時要注意鋼筋或夾具軸線是否在同一直線上，鋼筋是否裝置結實，過長的鋼筋裝置時應有置于同一水平面的延伸架，如機具損壞，特別是焊接夾具墊塊損壞應及時修理或替換，經檢驗合格后方準焊接；

　　2. Reinforcement processing equipment should be carried out by licensed welders. When installing reinforcing bars, attention should be paid to whether the axes of reinforcing bars or fixtures are on the same straight line, whether the reinforcing bars are strong or not, and if the reinforcing bars are too long, an extension frame should be placed on the same horizontal plane. If the machine tool is damaged, especially the damage of welding fixture pads should be repaired or replaced in time, and quasi-welded

　　3、依據《鋼筋焊接及檢驗規程》(JCJ18)合理挑選焊接參數，正確掌握操作方法。焊接完成后，應視狀況堅持冷卻1～2min后，待接頭有足夠的強度時再拆除機具或移動；

　　3. Reasonable selection of welding parameters and correct grasp of operation methods according to the Code for Welding and Inspection of Reinforcement Bars (JCJ18). After the welding is completed, the machine tool should be removed or moved after cooling for 1 to 2 minutes according to the condition, and when the joint has enough strength.

　　4、焊工有必要持有上崗證。鋼筋焊接前，有必要依據施工條件進行試焊，合格后方可施焊；

　　4. It is necessary for welders to hold a job certificate. Before welding, it is necessary to carry out trial welding according to construction conditions, and only after qualified can it be welded.

　　5、焊接完成后有必要堅持自檢。對接頭彎折和偏疼超過標準的及未焊透的接頭，應切除熱影響區后從頭焊接或采取補強焊接辦法；對脆性斷裂的接頭應按規定進行復驗，不合格的接頭應切除熱影響區后從頭焊接。

　　5. It is necessary to insist on self-inspection after welding. For joints with bending and migration exceeding the standard and incomplete penetration, the heat affected zone should be removed and then ab initio welding or reinforcing welding should be adopted; for joints with brittle fracture, the required re-inspection should be carried out, and for unqualified joints, the heat affected zone should be removed and ab initio welding should be adopted.

　　二、直螺紋絲扣加工缺陷

　　2. Machining Defects of Straight Thread Screw Bucks

　?。ㄒ唬┈F象：

　　(1) Phenomena:

　　絲扣殘缺、數量不行、絲頭端部不平整等（如圖1、圖2）。

　　Wire buckles are incomplete, the number is not good, and the end of the wire head is uneven (Fig. 1 and Fig. 2).

　?。ǘ┰蚱饰觯?/div>